| Home > Non-Asbestos > Gland Packing |
|
| |
|
NON ASBESTOS PACKINGS AND SEALS FOR PUMPS AND VALVE |
|
| |
| |
|
| |
| SUPERSEAL Style No. 900 |
A unique interbraided packing manufactured from pure graphite fibre with excellent heat dissipating properties and chemical resistance.
Service Media : Strong acids and alkalies, solvents, fuel and lube oils, super heated and saturated steam, bitumen, SO etc.
Working condition : Temp. 850°C, Pressure 400 KCS, PH range 0 to14 |
| |
| SUPERSEAL Style No. 901 |
Pure PTFE fibre interlock braided packing without having any additives.
Service Media : Food stuff, oxygen services, ammonia, carbonate solution, strong / weak acid and alkali etc.
Working Condition : Temperature –200°C to +260°C, Pressure 500 KCS, PH range 0 to 14. |
| |
| SUPERSEAL Style No. 902 |
 Pure PTFE interlock braided packing incorporating break in lubricant having high cross-sectional density.
Service Media : Corrosive gases, acids, ammonia, caustics, solvents, etc.
Working Condition : Temperature –200°C to +260°C, Pressure 500 KCS, PH range 0 to 14. |
| |
| SUPERSEAL Style No. 903 |
Pure PTFE filament interlock braided incorporating antifrictional inert lubricant.
Service Media: Acids and alkali, oils and any corrosive chemicals except flourine and molten alkalie metal.
Working Condition : Temp. - 200°C to + 250°C, Pressure 200 KCS, PH range 0 to 14 |
| |
| SUPERSEAL Style No. 904 |
Interlock braided Aramid / KEVLAR fibre braided packing incorporating break in lubricant and special fluoropolymer.
Service Media : Crystalline chemical slurries, ash slurry, any abrasive media, oil wood pulp, brines, organic solvents, hydrocarbon, sewage and hot water, coal and iron dust etc.
Working Condition : Temp. - 200°C to + 300°C, Pressure 500 KCS, PH range 0 to 13. |
| |
| SUPERSEAL Style No. 905 |
Pure carbon filament interlock braided packing firmly entrapping fine graphite flake as blocking agent to stop leakage.
Service Media : Acids, oils, solvents, super-heated steam, etc.
Working Condition : Temp. 550°C Pressure 180 KCS, PH range 0 to 14. |
| |
| SUPERSEAL Style No. 906 |
 Cross-braided combination packing manufactured for pure PTFE fibre and pure graphite fibre.
Service Media : Corrosive and non-corrosive gases, acids, oils, alkali solutions, oleum, etc.
Working Condition : Temp. 450°C Pressure 450 KCS, PH range 0 to 14. |
| |
| SUPERSEAL Style No. 907 |
PTFE intimately bonded with graphite packing in interlock braid.
Service Media : Caustics, acids, dyes and chemicals etc.
Working Condition : Temp. -200°C + 250°C, pressure 100 KCS, PH 0 to 14. |
| |
| SUPERSEAL Style No. 908 |
Interlock braided PTFE graphite solid yarn dense packing manufactured in single molecular structure.
Service Media : Mercury, acids and alkali, dyes and chemicals, oils and solvent, white and black liquor bitumen, boiler feed water, hydrocarbon, hypo etc.
Working Condition : Temp. -200°C to + 300°C. , Pressure 180 KCS, PH 0 to 14. |
| |
| SUPERSEAL Style No. 991 |
 Cross braided packing manufactured from combination of Aramid / KEVLAR fibre and graphited PTFE fibre.
Service Media : Mercury, alkaline solution, hot water, mild abrasive media, critical chemical compound, green liquor, etc.
Working Condition : Temp. -200°C to 300°C, pressure 250 KCS, PH 1 to 13. |
| |
| SUPERSEAL Style No. 992 |
Perfect combination inter-braided packing having graphite PTFE yarn as its base and aramid / KEVLAR yarn at the edges.
Service Media : Black and green liquor, sewage water, oil, weak acid and alkali, etc.
Working Condition : Temp. -200°C to +300°C, pressure 250 KCS, PH 1 to 13. |
| |
| SUPERSEAL Style No. 993 |
Interlock braided packing having pure PTFE fibre at the face and aramid / KEVLAR fibre at the corner.
Service Media : Carbonate solution, ammonia and ammonium compound, tri-sodium phosphate, DMT and host of critical chemicals used in petrochemical industries.
Working Condition : Temp. -200°C to +260°C, pressure 500 KCS, PH 1 to 13. |
| |
| Superseal packings are available in rope form as well as in preformed ring in oblique cut. |
| |
|
|
|
 |
|
 |
|
|